Our Conductive High-Temperature Silver/Carbon G6E-HTNS Epoxy has been developed for applications that require high-temperature operation (up to 316°C/600 F), excellent moisture and chemical resistance. Our G6E-NS series of epoxies has been developed based on advanced proprietary technology that requires less silver content to be at par with leading silver based epoxies in terms of electrical properties. This improvement makes G6E-NS less dense, more flexible, and allows for stronger adhesion to the target substrate. Carbon fillers add superior durability, fatigue and crack resistance along with low electrical resistance.
G6E-HTNS is a two-component electrically conductive adhesive that is engineered to combine bond strength and high electrical conductivity. The epoxy composite is based on the nanocarbon mixture and silver particles. The G6E-HTNS resin works in high temperature and demonstrates excellent adhesion to a variety of materials including plastics, metals, glass and ceramics. It offers superb resistance to moisture, solvents and oxidants as well as exceptional durability. The G6E-HTNS adhesive can be used as a solder replacement for applications where heating the component is desirable.
. TWO COMPONENT SYSTEM: Part A – smooth dark grey paste, Part B – smooth thixotropic silver paste.
. THE MIX RATIO: Mix 100 (Part A) to 100 (Part B) by weight.
. CURING INSTRUCTIONS: Best results are obtained when the product is cured at one of the following schedules: 4 hours @ 150°C (302 F). For optimum properties, post cure for 1-2 hours @ 180°C (350 F).
. COLOR: Silver Grey
. POT LIFE: 4 hours
. GLASS TRANSITION TEMPERATURE: 140°C
. MIXED VISCOSITY: 220-230 Pa·sec at 25°C/77 F
. HARDNESS, SHORE >83D
. VOLUME RESISTIVITY: ~ 0.003 Ω·cm
. OPERATING TEMPERATURE: Up to 316°C (600 F)”