Conductive epoxies can be used to form an electrically conductive bond between dissimilar materials eliminating the need for soldering. Traditional silver-based epoxy materials require up to 80% weight load of silver fillers and as a result tend to be costly, brittle and prone to mechanical failure.
Silver/Carbon Epoxy G6E-NS10 is a two component adhesive for high performance bonding, sealing and coating purposes. G6E-NS10 is intended to be cured at elevated temperatures. It can cure at room temperature in 60 hours or much more rapidly at elevated temperatures. Recommended curing temperature is 150°C. Volume resistivity of as low as 0.005 Ω·cm can be achieved under optimum curing conditions.
. TWO COMPONENT SYSTEM: Part A – smooth thixotropic dark grey paste, Part B – smooth thixotropic silver paste.
. THE MIX RATIO: 100 (Part A) to 100 (Part B) by weight.
. CURING INSTRUCTIONS: Best results are obtained when product is cured at one of the following parameters: 60 hours @ 25°C, 3 hours @ 70°C or 1 hour @ 150°C
. COLOR: Silver grey
. POT LIFE: 4 hours
. GLASS TRANSITION TEMPERATURE: 103°C (cured at 150°C)
. MIXED VISCOSITY: 150 – 155 Pa·s at 25°C/77 F
. HARDNESS, SHORE: >60D
. VOLUME RESISTIVITY: ≤ 0.005 Ω·cm